Products Description
The main components of Dawn BF1112 grade Modified Biodegradable PBAT Resin are PLA, PBAT and starch. Due to the large proportion of starch, its price is relatively cheap, and its mechanical properties and use can meet the requirements of conventional packaging bags and film materials. BF1112 Modified Biodegradable PBAT Resin degrades quickly and at a low price.
If you are looking for an affordable biodegradable raw material that can be directly used in blown film processing to make all kinds of film products, this is the right one!
Products Parameters
| Performance | Value |
| Density / g/cm3 | 1.30 |
| MFR / g/10min | 4.8 |
| Tensile Modulus / MPa | 205.5 |
| Tensile Strength / MPa | 14.4 |
| Elongation at Break / % | >400 |
Processing instructions
Modified Biodegradable PBAT Resin can be processed using conventional extrusion and injection molding techniques. The recommended processing temperature is between 170-200°C, depending on the processing equipment and the desired properties of the final product. The processing conditions can be optimized to achieve a wide range of mechanical properties and surface finishes.
Products application
Due to the increasing environmental awareness of mankind, Modified Biodegradable PBAT Resin with biodegradable properties are ideal materials for packaging applications to reduce the impact of packaging on the environment.
If you don't have the equipment and conditions for modification, you can directly choose Dawn's BF1112 starch-filled fully biodegradable blown film modifier.